Release Paper for Adhesive Coating
Solventless or solvent based; suitable for acrylic adhesive coating.
Good release stability, good flatness, high SUB. Adhesion.
Single Side or Double Sides Coated
Suitable for label, advertising inkjet coating, all kinds of packaging, adhesive lamination
Solventless — Solvent-free, non-VOC, suitable for automatic labeling, peeling force is less compared to solvent-based
Solvent based — backing can be glassine paper, kraft paper, art paper, woodfree paper, etc.
Surface Material | Color | Thickness | Release Force-TESA(g/inch) | Description |
Yellow Kraft Paper | Brown/yellow | 75-150 | 10-60 | self-adhesive/ Liner |
White Kraft Paper | White | 60-140 | Single-sided , double-sided | |
White Halftone Paper | White | 80-160 | Smooth Make the glue surface more evenly | |
Glassine Paper | Blue/White | 65-130 | Specialty Temperature Range |
Release paper for TPU
Good flatness, temperature resistance and stiffness
Has good flatness, good waterproof and moisture-proof, good anti-static property, good anti-fouling property
TPU hot melt film coating, special release paper for laminating film
Surface Material | Color | Basic Weight (µm) | Release Force-TESA(g/inch) | Description |
Glassine Paper | White | 80~90g | 50~200 | Hot melt film universal type |
80~90g | 600~1200 | Special heavy unwinding force | ||
CCK | 120g | 400 | Stiffness & Temperature Range requirements |
Release paper for carbon-fiber-resin prepreg
High temperature resistance, moisture resistance
Can put in the freezer after hot melt glue impregnation
Carrier for carbon fiber one-directional UD、weaving prepreg process
Separater during woven prepreg impregnation process
Surface Material | Color | Basic Weight (µm) | Release Force-TESA(g/inch) | Description |
CCK | White | 120 | 20-50 | Dedicated for hot melt equipment |
Glassine Paper | 80 | 15 | For stacking impregnation intervals | |
Brown kraft paper | Brown | 20 |