Fiberglass Tape

 Anti-shock、high-temperature resistant

 Surface protection tape for spraying and sandblasting in industrial and electronic industries

Material Thickness(µm)

Color

180° Peel Adhesion

(kg/inch)

Adhesive Base

Temperature Range(°C)

Glass cloth 90um

Off-white

1.0↑

Silicone

260

UV Tape

 After irradiating UV ultraviolet light, the adhesive force is greatly reduced, so that the object is easily separated from the adhesive without leaving residue.

 The tape used for Wafer, glass dicing, back grinding, miniature Copper Foil, PCB cutting, and can be easily removed after finishing the productions process.

Material Thickness(µm)

Color

180° Peel Adhesion

(kg/inch)

Adhesive Base

Temperature Range(°C)

PET 50↑
PO 140 150

Transparent
Matte

200~2000

(before)
50↓(after)

Acrylic

60

Thermal Release Tape

 With the adhesive at room temperature, the use of temporarily fixing the process to avoid displacement or batch carry-over, and while finishing the productions process, the tape can be easily removed by heating up to reduce the Adhesion Force.

 Used for the protection and bearing processes such as Wafer, glass, Ceramic require back grinding, polish, dicing etc.

Material Thickness(µm)

Color

180° Peel Adhesion

(kg/inch)

Adhesive Base

Temperature Range(°C)

PET 50

Transparent

 1000

Acrylic

100

Cooling Stripping Type Protective Film

 The Adhesion Force can be increased by heating up to prevent the process from stripping off. And it will return to the original adhesive to be easily removed when the temperature is cooling down.

 It is suitable for fixing the manufactured products in the thermal process, such as Passive components, Ceramic components layering, dicing, etc.

Material Thickness(µm)

Color

180° Peel Adhesion

(kg/inch)

Adhesive Base

Temperature Range(°C)

PET 36↑

Matte

10↓

(before)
100~1500

(after)

Acrylic

130